Description
Grade: 2507
Thickness: 0.3-3.0mm
Width: 1219,1500mm
Tolerance: Thickness: ±0.02mm Length: ± 5mm
Brand : BAOSTEEL,TISCO,ZPSS
Standard: ISO,ASTM,SUS,GB
Surface: 2B,BA,NO3,NO4
Place of origin: China (mainland)
Payment terms : L/C at sight or 30% TT as deposit
Standards
ASTM/ASME:A240 - UNS S32750
EURONORM:1.4410 - X2 Cr Ni MoN 25.7.4
AFNOR:Z3 CN 25.06 Az
DIN/EN 1.4410,ASME SA-240
Duplex 2507 (UNS S32750) is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity, and a low coefficient of thermal expansion. The high chromium, molybdenum, and nickel levels provide excellent resistance to pitting, crevice, and general corrosion.
Chemical Properties
Mechanical Properties
1. 2507 duplex stainless steel pipe mechanical properties at room temperature
Pipe:thickness≤20mm ;δb/MPa:800-1000 ,δ0.2/MPa:≥550 ,δ5/%:≥25 ,(HV):290
2 .2507 duplex stainless steel plate in the mechanical properties of room temperature of -200 ℃ :
/℃ δb/MPa
Room Temperature ≥530
Sheet 100 ≥450
200 ≥400
3. Mechanical properties of 2507 large-diameter seamless tube
Dia*thickness δb/MPa δ0.2/MPa δ5/% (HV)
273.0mm×4.19mm 894 644 40 284
323.9mm×4.57mm 858 662 45 270
406.4mm×4.74mm 854 657 41 272
Corrosion
General Corrosion
1). high chromium and molybdenum content of 2507 makes it extremely resistant to uniform corrosion by organic acids like formic and acetic acid.
2). provides excellent resistance to inorganic acids, especially those containing chlorides.
3). can be used in dilute hydrochloric acid.
4). Pitting need not be a risk in the zone below the borderline in this figure, but crevices must be avoided.
Intergranular CorrosionStress
1). Low carbon content greatly lowers the risk of carbide precipitation at the grain boundaries during heat treatment.
2). Is highly resistant to carbide-related intergranular corrosion.
Corrosion Cracking
1). Duplex structure of 2507 provides excellent resistance to chloride stress corrosion cracking (SCC).
2). Superior to 2205 in corrosion resistance and strength.
3). 2507 is especially useful in offshore oil and gas applications and in wells with either naturally high brine levels or where brine has been injected to enhance recovery.
Pitting Corrosion
Different testing methods can be used to establish the pitting resistance of steels in chloride-containing solutions.
Crevice Corrosion
Highly resistant to crevice corrosion.
Our Services
1.Professional person communicate with you before the order
2.OEM&ODM, also provide customized service
3.Offer for your unique design and some our current model
4.Protection of your sales area, ideas of design and all your private information
5.Provide strict quality check for each part,each process before export
6.Provide complete post-sale service,including installation,technical guide
Recommend commodities
Chat Online